Dn24'' Heat Shinrkable Wraparound Sleeve
Heat shrinkable sleeve (2 layers), which are developed and manufacture for Anti-corrosion of pipeline, are the composition of radiation cross-linked Polyethylene backing and high shearing strengthen melt adhesive, and have The function of shape memory. The hot melt adhesive is squeezed into the Joint by the shrink power to form a perfectly sealed surface, after being Heated. It is compatible with standard pipe coating, also can be used for Coating bare, replacement pipe section and large radius bends. The system Is designed to be applied with minimum preheating and is ideal for large Diameter wastewater pipe.
Feature
Fast shrinkage speed, good waterproof performance, good anti-corrosive Performance, long service life, convenient transportation and fast Construction. The product are ideal material for corrosion prevention and Insulation.
Application scope
It's mainly used for heat pipe network, steel pipe corrosion resistance and Insulation, chemical pipes and sewage pipes etc.
Used for protection of welded joints of oil, water & gas pipelines from Mechanical damage & corrosion.
Technical Datas
Sleeve Operating Characteristics |
Test Method |
|
Test Result |
Pipeline Operating Temp. |
|
|
Up to 65°C |
Minimum Installation Temp. |
|
|
75°C (140°F) |
Mainline Coating Compatibility |
|
|
PE,PP, FBE,HPPC |
Adhesive Properties |
Softening Point |
ASTM E28 |
|
100°C |
Lap Shear @ 23°C |
DIN 30672 |
|
79 N/cm2 |
Backing Properties |
Tensile Strength |
ASTM D638 |
|
21MPa |
Elongation |
ASTM D638 |
|
500% |
Hardness |
ASTM D2240 |
|
50 Shore D |
Volume Resistivity |
ASTM D257 |
|
1017 ohm-cm |
Sleeve Properties |
Peel Strength @ 23°C |
DIN30672 |
|
96 N/cm |
Impact Resistance |
ASTM G14 |
|
56Inch.LBS |
Indentation Resistance |
ISO 21809-3 |
|
0.65mm |
Cathodic Disbondment @ 23ºC, 28 days with epoxy |
ASTM G8 |
|
9 mm rad |
Low Temp. Flexibility |
ASTM D2671-C |
|
-32°C |