Radiation Cross Linked 3PE Hot Shrinkable sleeve for Joint Weld
HSWS, Two-piece, with separate closures designed for the corrosion protection. HSWS is superior performance heat shrinkable products designed for corrosion protection on field applied girth-weld joints of buried and exposed steel pipelines operating up to 80° C (176° F).
The inner layer is two-components epoxy primer which coated on steel pipe;
Intermediate level is special hot melt adhesive;
Outer layer is modified radiation crossing linking polyethylene backing.
Features & Benefits:
Heat Shrinkable Sleeves provide great corrosion protection, Superior resistance to Cathodic Disbondment and excellent durability against abrasion and chemical attack. The result is effective, good performance of sealing, wide application, easy to operate and preheating temperature low (50 celsius degree), long term protection against corrosion.
Saves time& money
Rapid & reliable Installation
Long term protection
HSWS is a wraparound sleeve with a separate closure
Cross-linked backing provides superior abrasion, mechanical and chemical attack resistance.
High performance adhesive provides excellent resistance to Cathodic Disbondment to ensure long-term corrosion protection.
Just-in-time customized lengths allow bulk rolls to be field cut to protect any pipe size
Open sleeve configuration allows the product to be applied after the pipeline has been welded and cleaned.
Pipeline size: From Ø 108 to Ø 1554 (4''---60'')
Sleeves width: 100mm, 150mm, 200mm, 300mm, 450mm, 500mm, 600mm, 650mm
Sleeves Thickness: 1.8mm, 2.0mm, 2.2mm, 2.5mm, 2.8mm
Closure patch: 100mm, 150mm, 200mm (4'', 6'', 8'')
Model: HSWS 3600/505/ Ø 1066.8
HSWS--Heat shrinkable wraparound sleeves
505----- -Roll Width (as supplied)
Ø 1066.8----Joint or pipeline Diameter
|Sleeve Operating Characteristics||Test Method|| ||Test Result|
|Pipeline Operating Temp.|| || ||Up to 80°C |
|Minimum Installation Temp.|| || ||110°C (140°F)|
|Mainline Coating Compatibility|| || ||PE,PP, FBE,HPPC|
|Softening Point||ASTM E28|| ||140°C|
|Lap Shear @ 23°C||DIN 30672|| ||180 N/cm2|
|Tensile Strength||ASTM D638|| ||24MPa|
|Elongation||ASTM D638|| ||480%|
|Hardness||ASTM D2240|| ||50 Shore D|
|Volume Resistivity||ASTM D257|| ||2x1016 ohm-cm|
|Peel Strength @ 23°C||DIN30672|| ||80 N/cm|
|Impact Resistance||ASTM G14|| ||56Inch.LBS|
|Indentation Resistance||ISO 21809-3|| ||0.65mm|
|Cathodic Disbondment @ 23ºC, |
28 days with epoxy
|ASTM G8|| ||4mm rad|
|Low Temp. Flexibility||ASTM D2671-C|| ||-32°C|